It has been proved that these cracks are caused by sulfidestresscorrosioncracking (SSCC) through failure analysis and service environment survey.
通过失效分析和管道服役环境调查,证明开裂原因是管道服役期间发生硫化物应力腐蚀开裂(SSCC)。
2
The mechanism and general influence factors of sulfidestresscorrosioncracking (SSCC) of chemical equipment made of high strength steel are summarized.
系统的综述了高强钢化工设备硫化物应力腐蚀开裂机理及常规的影响因素。
3
Based on the NACE standard, the behavior of restriction on hydrogen induced cracking (HIC) and sulfidestresscorrosioncracking (SSCC) of X80 grade pipeline steel was investigated.