This research USES rough sets to reduce this factors, then adopts radial basis function networks to predict and diagnose the continuous casting slab defect.
提出用粗糙集理论简化这些因素，然后采用径向基函数网络对连铸板坯缺陷进行预报诊断。
2
It is considered that the temperature fluctuation of meniscus is a key factor for the surface defect formation of continuous casting billets.
据此认为，连铸弯月面温度波动是导致铸坯表面缺陷产生的一个重要原因。
3
Centerline shrinkage is the main defect that affects the inner quality of continuous casting slab.