The deformation of near a titanium alloy at RT is controlled by dislocation slip while at 20k is under the mutual control of dislocation slip and twinning.
近以钦合金的室温变形主要由位错滑移控制，20 K下的变形则由位错滑移和孪生变形共同控制。
2
Deformationtwinning of cast magnesium alloy AM60 was investigated by compression at room temperature with various deformation degrees from 3.
在电子万能试验机上对铸态am 60镁合金进行室温压缩试验，研究了在变形量分别为3。
3
The microstructure of Twinning Induced Plasticity (TWIP) steel during tensile deformation was investigated with SEM and TEM.