The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
研究表明该钢具有较好的抗应力腐蚀性能，其应力腐蚀断裂形貌为穿晶、解理断裂，并有二次裂纹。
2
The results showed that it was chlorine ion that resulted in transgranular stress corrosion cracking in brass tubes.