The effect of melt overheating treatment on the solidification segregation of M963 cast Ni-base superalloy has been studied.

Is mainly the size effect and solidification, shrinkage, stress and other issues clearly, to avoid or reduce the segregation, iron manhole cover deformation and crack defects.

It was summarized in present paper that the liquid flow acted in the transfers process, solidification structure and componential segregation.