The results show that the wheel hub cracking during radial impact testing was caused by excessive content of magnesium in the alloy as well as the overheating of the alloy during the solution process.
The results show that the wheel hub cracking during radial impact testing was caused by excessive content of magnesium in the alloy as well as the overheating of the alloy during the solution process.