Uneven components of quenchedmartensite and residual austenite structure and improper grinding parameter are attributed to the main causes for cracks.
淬火组织中马氏体与残余奥氏体的成分不均匀及磨削用量参数选择不当是导致裂纹出现的主要原因。
2
The results show that there are four kinds of carbides in annealed state of the steel, and major portion of quenchedmartensite is lath-like martensite.
结果表明，该钢退火状态存在四种类型碳化物，淬火组织以板条马氏作为主。
3
The large welding current caused the formation of quenchedmartensite and the high residual stresses in the welding zone, resulting in the increase of zinc sensitivity of hydrogen attack.