In the first cracking stage grainboundary released more hydrogen than in the second stage.
而微空洞释氢则第二阶段多于第一阶段。
2
The main reason for cracking is liquid copper diffused into the austenite grainboundary and grain boundary embrittlement was caused, so the welded pipe cracked under stress.