Through-thickness cracking also can lead to fatigue or stress corrosioncracking of the base metal beneath the plating.
还会形成穿透型裂纹，造成镀层下本体金属的疲劳或应力腐蚀裂纹。
2
Stress concentrations can lead to initiation of cracking by fatigue, stress corrosion, or hydrogen-assisted stress corrosion.
应力集中可能会导致疲劳、应力腐蚀或氢基应力腐蚀而产生裂纹。
3
The fracture and the surface of a hip joint fractured invivo has been studied by SEM. It is concluded that the fracture was due to corrosionfatiguecracking by bending stress.