The formation mechanism of bulging and cracking of combustor inner liner and his influence on gas turbine exhaust temperature dispersity was analyzed.

Moreover, they are able to decrease the temperature and increase the stress of hot cracking formation, as a result, decrease the tendency of hot cracking.

These conclusions are important theory to guide the study of the formation mechanism of cold cracking in the two sides of fusion line of dissimilar steel welded joint.