The occurrence of high shear stress at the fibre end is a factor which is expected to lead to crack generation .
在纤维端部存在高切变应力视为导致产生裂缝的因素。
2
The results show that the fibre orientation affects on the stress corrosion cracking of GRP seriously.
结果表明，纤维取向对玻璃纤维增强塑料的应力腐蚀行为有很大影响。
3
The effect on shrinkage deformation of fibre winding composites were considered by discussing the winding tensile resin thermo-shrinkage stress and the mandrels.